ASTM A1090_A1090M-24
Standard Specification for Forged Rings and Hollows for Use as Base Plates in Power Transmission Structures
| Standard number: | ASTM A1090_A1090M-24 |
| Released: | 15.10.2024 |
| Status: | Active |
| Pages: | 3 |
| Section: | 01.05 |
| Keywords: | atmospheric corrosion resistance; bars; bolted construction; bridges; buildings; durability; forgings; high strength; low alloy; riveted constructions; shapes; steel; structural steel; weight; welded construction; |
| ASTM number: | ASTM A1090/A1090M |
| Supersedes: | A1090_A1090M-19R24 |
This specification is intended for high-strength, low-alloy forged rings and hollows produced from steels with atmospheric corrosion resistance for use as base plates in welded tubular structures. These steels have considerably better atmospheric corrosion resistance in most environments than carbon structural steel with or without copper addition, and are suitable for many applications in the bare (unpainted) condition when exposed to the atmosphere. The standard covers ordering information and general requirements for delivery, materials and manufacture, heat treatment, mechanical requirements, and the material's chemical composition.
1.1 This specification covers high-strength, low-alloy steel ring and hollow forgings intended primarily for use as base plates in welded tubular structures for power transmission applications. However, use of this specification is not restricted to such applications and it may be used in other applications for which the attributes of the materials, as defined by this specification, are appropriate.
1.2 The atmospheric corrosion resistance of Grades A, B, and C in most environments is substantially better than that of carbon structural steel with or without copper addition (see Note 1). When exposed to the atmosphere, these grades are suitable for many applications in the bare (unpainted) condition.
Note 1: See Guide G101 for methods of estimating the atmospheric corrosion resistance of low-alloy steels.
1.3 The thickness of forgings is limited only by the capacity of the composition to meet the specified mechanical property requirements; however, current practice normally limits the thickness of forgings furnished under this specification to a range of 2 in. to 6 in. [51 mm to 152 mm].
Note 2: When the steel is to be welded, a welding procedure suitable for the grade of steel and intended use or service should be used. See Appendix X3 of Specification A6/A6M for information on weldability.
1.4 The text of this specification contains notes, footnotes, or both, that provide explanatory material. Such notes and footnotes, excluding those in tables and figures, do not contain any mandatory requirements.
1.5 Supplementary requirements are available but shall apply only when specified by the purchaser at the time of ordering.
1.6 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system are not necessarily exact equivalents; therefore, to ensure conformance with the standard, each system shall be used independently of the other, and values from the two systems shall not be combined.
1.7 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.
1.8 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.