ASTM D5572-95R19
Standard Specification for Adhesives Used for Finger Joints in Nonstructural Lumber Products
| Standard number: | ASTM D5572-95R19 |
| Released: | 01.02.2019 |
| Status: | Active |
| Pages: | 17 |
| Section: | 15.06 |
| Keywords: | adhesive; bonded; dry use; finger joint; flexure; nonstructural; tension; wet use; |
| ASTM number: | ASTM D5572 |
| Supersedes: | D5572-95R12 |
This specification establishes the performance levels for adhesives to be used in finger joints in nonstructural bonded-lumber products. Such products include, but are not limited to, interior and exterior mouldings, window and door components or parts, and bonded-lumber panels. The apparatus shall consist of environmental chamber for moist-heat aging, oven with sufficient air circulation to remove moisture from the chamber, tanks for soaking and boiling, testing machines for the flexure and tension specimens, and vacuum-pressure vessel. Tests shall be conducted such as dry, soak, elevated-temperature, and temperature-humidity tests for dry-use classification and dry, boil, elevated-temperature, and vacuum-pressure tests for the wet-use classification. The adhesives shall be tested for performance which shall meet the following requirements: moisture content; specific gravities of wood species; tensile strength; wood failure for soft and hard woods; and rupture modulus.
1.1 This specification establishes performance levels for adhesives to be used in finger joints in nonstructural bonded-lumber products. Such products include, but are not limited to, interior and exterior mouldings, window and door components or parts, and bonded-lumber panels. Adhesives that meet the requirements of the various performance classes are considered capable of providing an adequate bond for use under the conditions described for the class. This specification is to be used to evaluate adhesives as well as the adhesive bonds in the finger joints. See Section 5, Significance and Use, for limitations when using this specification to evaluate industrially manufactured finger joints.
Note 1: This specification supersedes the finger-joint portion of the 1990 edition of Specification D3110.
1.2 The following index is provided as a guide to the test methods in this specification:
|
| Section |
| Apparatus | 6 |
| Equipment, Material, and Preparation of Assemblies and Specimens | 7 |
| Conditioning for Factory-Manufactured Assemblies, Laboratory-Made Assemblies, and Test Specimens | 8 |
| Testing in Flexure | 9 |
| Testing in Tension | 10 |
| Exposure Conditions and Treatments | 11 |
| 1. Dry Use Tests: Dry, 3-cycle Soak, Elevated Temperature, and Temperature-Humidity | 11.1 |
| 2. Wet Use Tests: Dry, Boil, Elevated Temperature, and Vacuum-Pressure | 11.2 |
Note 2: The conditioning needed for various stages in the preparation of both types of specimens and for the exposure tests are given.
Note 3: Specific guidelines for specimen size, exposure conditions, testing, calculation, and reporting are given for flexure specimens in Sections 9 and 11, and for tension specimens in Sections 10 and 11.
1.3 For the definitions of dry use and wet use, see 3.2.1.1 and 3.2.1.2.
1.4 The values stated in inch-pound units are to be regarded as standard. The SI units given in parentheses are for information only.
1.5 The following precautionary caveat pertains only to the apparatus and test methods portions, Sections 6 – 11 of this specification: This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.
1.6 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.