ASTM A0739-90AR22
Standard Specification for Steel Bars, Alloy, Hot-Wrought, for Elevated Temperature or Pressure-Containing Parts, or Both
| Standard number: | ASTM A0739-90AR22 |
| Released: | 01.03.2022 |
| Status: | Active |
| Pages: | 2 |
| Section: | 01.05 |
| Keywords: | alloy steel bars; high-temperature applications; hot-wrought steel bars; pressure-containing parts; steel bars; temperature service application—high; |
| ASTM number: | ASTM A739 |
| Supersedes: | A0739-90AR16 |
This specification covers hot-wrought, ferritic alloy steel bars for elevated temperature or pressure-containing parts suitable for fusion welding or both. The bars are furnished in two grades: Grade B 11 and Grade B 22. The steel shall be made by on or more of the following primary processes: open-hearth, basic-oxygen, or electric furnace. The bars shall be normalized and tempered. The heat analysis shall conform to the limits for chemical composition specified. The bars as represented by the test specimen shall conform to the tensile requirements specified.
1.1 This specification2 covers hot-wrought, ferritic alloy steel bars for elevated temperature or pressure-containing parts suitable for fusion welding or both.
1.2 The bars are furnished in the following grades:
| Grade B 11: 1.25 % chromium, 0.55 % molybdenum |
| Grade B 22: 2.25 % chromium, 1.00 % molybdenum |
1.3 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.