BS EN 3976:2006 Aerospace series. Titanium and titanium alloys. Test method. Chemical analysis for the determination of hydrogen content

BS EN 3976:2006

Aerospace series. Titanium and titanium alloys. Test method. Chemical analysis for the determination of hydrogen content

Format
Availability
Price and currency
English Secure PDF
Immediate download
195.00 USD
You can read the standard for 1 hour. More information in the category: E-reading
Reading the standard
for 1 hour
19.50 USD
You can read the standard for 24 hours. More information in the category: E-reading
Reading the standard
for 24 hours
58.50 USD
English Hardcopy
In stock
195.00 USD
Standard number:BS EN 3976:2006
Pages:16
Released:2007-01-31
ISBN:978 0 580 50085 5
Status:Standard
DESCRIPTION

BS EN 3976:2006


This standard BS EN 3976:2006 Aerospace series. Titanium and titanium alloys. Test method. Chemical analysis for the determination of hydrogen content is classified in these ICS categories:
  • 49.025.30 Titanium
This standard specifies the requirements for chemical analysis using Inert Gas Fusion Thermal Conductivity Method for the determination of the hydrogen content of titanium and titanium alloys for aerospace applications. The method applies to hydrogen contents ranging from several micrograms per gram to several hundreds of micrograms per gram. It shall be applied when referred to in the EN technical specification or material standard unless otherwise specified on the drawing, order or inspection schedule. NOTE The absolute method not used in routine inspection is solid state hot extraction under vacuum followed by measurement of volume and pressure. Due to its complexity, it is only summarized in Annex A.